CRUSHING TESTS OF 6" WROUGHT IRON PIPE
Test Mark: No. 1 & No. 1
Distance between rounded knife edges No. When Pipe first began to crack. At commencement of test before application of load. 65/8" 1 bare 6" 1 fullNo loads measured.
Remarks.
The load was applied at a distance of 12" from the end of the Pipe.
The same Pipe was again tested but the load was applied at a distance of 2'8" from the other end, the Pipe being given a half turn in order to test the metal in both directions.
The Pipe was afterwards crushed down as far as the machine would allow, in order to further develop the cracks which had appeared when the knife edges were 4" apart.
Tests made in your presence on 19th October 1906.
sa astered) arada
253
SHEET
CRUSHING TESTS OF 6' WROUGHT IRON
PIPE
dfsqua 914 19vcl down a re238 00
osm DOW
10 c3 bour
R.H.H.S.
Test
Mark
Distance between rounded
knife edges
No.
When Pipe
3 13 ove.
VOY
YAMME .. .A
At commence- ment of test before application of loed.
first began
to crack.
29835
No. 1
65/8*
1
bare
29836
No. 1
G**
full
No loads measured.
禁站
Remarks.
The load was applied at a
distance of 12" from the end of the Pipe.
12-1
The same Pipe was again tested
but the load was applied at a distance of 2*8" from the other end, the Pipe being given
a half turn in order to test the metal in both directions.
The Pipe was afterwards crushed
down as far as the machine would allow, in order to further develop the cracka which had appeared when the knife edges were 4* apart.
Tests made in your presence on 19th October 1906.